Nitroflon

Product Characters

When metal with high speed friction to metal, noise will be happened and wearing rapidly, Nitroflon product with character of no applying lubricant required,the super lubricating result will be reached, it is guarantee that completely oiless (no more trouble of oil dirt to pollute surface of finished product).
Nitroflon with super high hardness alloy film, much lower noise, excellent sliding ability, excellent wearing-resistant, especially it is very good performance under heavy gravity,hardness is up to HV950 (HRC70.4), it is applicable for mirror surface, wire PIN, wearing consumable material, etc. related components, in order to match best functional surface treating technology.
Nitroflon is not only with high hardness non-oil lubricating performance, but also to enhance metal with super result of corrode-resistant under protection of special alloy film,it is capable of adding huge character on material to against corrosion, to resist acid & alkaline.
Special material of Nitroflon is suitable for any metal processing (copper, iron, steel, aluminum, etc..), method of material processing is also available for satin surface, shining surface, mirror surface, sand blasting, engraving, hair line, etc...

Applicable Range

It is able to coat on processing surface of various metal products, for example iron, steel, copper, aluminum, stainless steel, casting iron, powder metallurgy, etc…

Advantage

1

Even thickness of electroplating film and able to plate inside the hole without grinding process.

2

Plating layer with strong adhesion, high hardness, good corrode-resistant.

3

No oil apply required, no lubricant required.

4

Super lubricating performance, excellent sliding ability.

5

Alloy film with much lower noise

6

High hardness, wearing resistance is good.

7

Excellent corrode resistance.

Benefit

1

Hugely to reduce wearing

2

Extend the operation life.

3

Hugely to reduce cost.

4

Reduces percentage of defective product.

5

With idea of environment friendly.

Physical Character Comparison Sheet for Titaflon,Nitroflon and Hardened Chrome Coating

 

 

Nitroflon
(metal to metal)

Titaflon 
(metal to plastic)

Chemical Nickel

Hardened Chrome

Hardness
HV 1030~1060 HV 550 HV 450~500 HV 950~1000
Thermal-Resistance
500-700 ℃ 300-350 ℃ 400 ℃ 400 ℃
Sliding Ability
super excellent excellent good poor
Flow Ability
excellent super excellent no maker to apply it common
Separation Ability
excellent super excellent no maker to apply it common
Dynamic Friction Coefficient
0.045 0.058 0.114 0.118
Mold Release Ability
no mold release agent required no mold release agent required mold release agent not applied is possible must apply mold release agent
Corrode Resistance
PH 1~12 PH 1~12 PH 1~12 not workable
Equivalent Ability
±10 ±10 ±10 thickness is not same
Plating Surface
no micro hole no micro hole no micro hole cracking trend, more micro holes
Surface Roughness
0.02 0.27 0.12 0.44
 
 
Strong hardness good mold release ability